Glass windows often endure external environmental factors such as wind, rain, and humidity, which lead to the formation of microcracks in their surface. For instance, a gust of wind can propel sand onto a window and create microscale surface cracks due to the impact of sharp-edged sand particles. These microcracks then grow in size when aggravated by water droplets and humidity.
When water comes in contact with these surface flaws, it penetrates the microcracks and slowly dissolves the silicon-oxygen bonds. This chemical attack breaks the glass networks which gradually degrades the mechanical strength and optical properties of glass structures. This environmentally enhanced crack growth process is known as stress corrosion or subcritical crack growth (SCG). The depreciation of mechanical performance due to SCG raises safety concerns for skyscrapers and high-rise buildings.
Recently, scientists have taken an interest in the effect of SCG on two widely used types of soda-lime glass: annealed and tempered glass. However, most studies have focused on establishing crack growth rates, and not much is known about the effect of water on the propagation of crack flaws. Additionally, many of the studies investigated the microcrack propagation dynamics of annealed glass and not tempered glass.
To address this gap in research, a team of researchers from Pusan National University (PNU) led by Prof. Sanghu Park, explored the mechanisms associated with water-promoted cracking behavior around surface micro flaws in both annealed and tempered glass in a study published in the Journal of the European Ceramic Society. Prof. Park explains, "Thermally tempered glass is of great commercial importance; it is used in displays, protection covers, vehicular windows, and others. The crack propagation of tempered glass is different from that of annealed glass by water droplets. So, it's really important to understand how water droplet promotes cracking behavior in different types of glasses."
To emulate surface microcracks, the researchers created artificial flaws on a glass surface using a Vickers indenter—an instrument used to test the hardness of a material. Then, the samples were exposed to atmospheric humidity and water to analyze crack growth. The team discovered that the maximum length of crack growth was much lower in tempered glass than annealed glass. A subsequent 24-hour water immersion text revealed the formation of radial cracks in annealed glass and lateral cracks in tempered glass.
The comparative study provides new insights into the origin of glass cracks which can be useful for glass designers, engineers, and architects. "With an increase in typhoon and storm frequencies due to global warming, we need to find out new ways to protect the exterior of glass windows. We tried to understand the interactions between water and surface cracks to help solve safety problems associated with glass windows and structures," concludes Prof Park. Explore further Gorilla Glass, used for cell phones, is coming to cars More information: Hong-Seok Kim et al, Vickers crack extension and residual fracture strength of annealed and thermally tempered glass in water, Journal of the European Ceramic Society (2021). DOI: 10.1016/j.jeurceramsoc.2021.11.058 Provided by Pusan National University Citation: Study 'cracks' mystery of water-promoted fracture growth on glass (2022, January 12) retrieved 12 May 2022 from https://phys.org/news/2022-01-mystery-water-promoted-fracture-growth-glass.html This document is subject to copyright. Apart from any fair dealing for the purpose of private study or research, no part may be reproduced without the written permission. The content is provided for information purposes only.
More from Physics Forums | Science Articles, Homework Help, Discussion
Use this form if you have come across a typo, inaccuracy or would like to send an edit request for the content on this page. For general inquiries, please use our contact form. For general feedback, use the public comments section below (please adhere to guidelines).
Please select the most appropriate category to facilitate processing of your request
Thank you for taking time to provide your feedback to the editors.
Your feedback is important to us. However, we do not guarantee individual replies due to the high volume of messages.
Your email address is used only to let the recipient know who sent the email. Neither your address nor the recipient's address will be used for any other purpose. The information you enter will appear in your e-mail message and is not retained by Phys.org in any form.
Get weekly and/or daily updates delivered to your inbox. You can unsubscribe at any time and we'll never share your details to third parties.
Medical research advances and health news
The latest engineering, electronics and technology advances
The most comprehensive sci-tech news coverage on the web
This site uses cookies to assist with navigation, analyse your use of our services, collect data for ads personalisation and provide content from third parties. By using our site, you acknowledge that you have read and understand our Privacy Policy and Terms of Use.